304/304L/304H Stainless Steel Plate & Sheet Stockist In China

304/304L/304H STAINLESS STEEL PLATE

304/304L/304H stainless steel plate is one of the most popular stainless steel grades and Ronsco is proud to exported it to more than 80 countries.

GET A QUOTE or Download Spec Sheet

MORE DETAILS ABOUT 304/304L/304H STAINLESS STEEL PLATE

Product Name	304/304L/304H Stainless Steel Plate, 304/304L/304H Stainless Steel Sheet
Equivalent Grade	304: AISI 304, UNS S30400, SAE 304, DIN 1.4301, SUS 304, X5CrNi18-10
	304L: AISI 304L, UNS S30403, SAE 304L, DIN 1.4306, SUS 304L, X2CrNi19-11
	304H: AISI 304H, UNS S30409, SAE 304H, DIN 1.4948, SUS 304H, X6CrNi18-10
Standard	GB, AISI, ASTM, DIN, EN, JIS
Process	Hot Rolled, Cold Rolled, Forged
Sizes	Thickness: 0.3-200mm, Width: 10-4000mm
Surface Treatment	NO.1, 1D, 2D, 2B, NO.4, BA, HL, Mirror, Embossim, Sandblasted
Fabricating	Rolling, Bending, Slitting, Decoiling, Cutting, Drilling, Punching, Beveling, Welding etc.
Application	Oil&Gas, Petroleum, Vessels, Ship Building, Water Treatment And Environmental Protection etc.

GENERAL INFO ABOUT EACH Stainless Steel Plate GRADE

304/304L/304H stainless steel plate is one of the most widely used austenitic stainless steel grades. The grades shows high strength, excellent corrosion resistance and outstanding formability than any other grade of stainless steel. It is frequently utilized in oil and gas industries etc..

Single Sheet Of Rolling Specification
Thickness/Width	1500	1800	2000	2200	2400	2500	3200
4-6mm	√	√	-	-	-	-	-
6-10mm	√	√	√	√	√	-	-
11-12mm	√	√	√	√	√	√	√
13-14mm	√	√	√	√	√	√	√
17-25mm	√	√	√	√	√	√	√
26-70mm	√	√	√	√	√	√	√
71-120mm	special	special	special	special	special	special	special

MORE DETAILS ABOUT EACH Stainless Steel Plate GRADE

Hot Forming
Cold Forming
Welding

304/304L/304H Stainless Steel Grade:

For maximum corrosion resistance, the material should be annealed at 1900°F (1038°C) minimum and water quenched or rapidly cooled by other means after hot working.

304/304L/304H Stainless Steel Grade:

It is quite ductile and forms easily. Cold working operations will increase the strength and hardness of the alloy and might leave it slightly magnetic.

304/304L/304H Stainless Steel Grade::

It can be readily welded by most standard processes.

CHEMICAL PROPERTIES

	C	Mn	P	S	Si	Cr	Ni	Mo	N	Cu
304	0.07	2.00	0.045	0.03	0.75	17.50-19.50	8.00-10.5	/	0.10	/
304L	0.03	2.00	0.045	0.03	0.75	17.50-19.50	8.00-12.00	/	0.10	/
304H	0.10	2.00	0.045	0.03	0.75	17.50-19.50	8.00-10.5	/	0.10	/

MECHANICAL PROPERTIES

	Tensile Strength (min)		Yield Strength (min)		Elongation	Hardness, max
	ksi	Mpa	ksi	Mpa	/	Brinell.HBW	Rockwell
304	75	515	30	205	40	201	92HRBW
304L	70	485	25	170	40	201	92HRBW
304H	75	515	30	205	40	201	92HRBW

MORE DETAILS ABOUT EACH Stainless Steel Plate PROCESS

Steel Making Process
Hot Roll Process
Solid Solutions & Pickling

MORE DETAILS ABOUT EACH Stainless Steel Plate SURFACE

NO.1
2D
2B
NO.4
BA
HL
Mirror

NO.1 surface treated by heat treatment and pickling after hot rolling. The appearance is silver white, matt and bright. This surface is suitable for industries that require heat resistance and corrosion resistance, and the surface brightness is not important. Common applications include industrial tank and chemical industrial plants etc..

2D surface treated by heat treatment and pickling after cold rolling. The appearance is silver white, smoother but of matt grain. Common applications include petrochemical production equipment, automotive components, building materials and water pipes etc..

After 2D treatment, the final process is lightly cold rolled by a polishing roller to obtain proper gloss. The appearance is smooth and bright, and easy to re-grind to make the surface more brighter. Common applications include building materials, tableware etc..

NO.4 is a product ground with a grinding belt of size 150-180. It has better gloss, discontinuous rough lines and finer stripes than No.3 stainless steel castings commonly used polished and sanded surfaces. Common applications include food processing equipment, home electrical products, medical equipment etc..

BA surface is also produced by cold rolling and de-scaling. It has excellent surface gloss, high reflectivity. In addition, The very smooth surface also makes this surface highly suitable for further finishing processes such as mirror polishing and chrome plating. Common applications include catering equipment etc..

HL use a polishing abrasive belt with an appropriate particle size (150-320 mesh) to grind, with obvious straight stripes. The surface is beautiful, good texture and scratch is not obvious, durable, wear-resistant. Common applications include building decoratio, elevators, vehicle parts, etc..

Mirror is produced by polishing with successively finer abrasives and buffing extensively until all grit lines from preliminary grinding operations are removed. The feature is highest reflectivity. Mainly used for interior and exterior decoration materials of automobiles and buildings.

FREQUENTLY ASKED QUESTIONS

What Is The Difference Between 304, 304L And 304H?
Why Is 304L Easier To Weld Than 304?
What Is The Yield Strength Of This Grade Stainless Steel?

What Is The Difference Between 304, 304L And 304H?

Answer:

304 is considered the most versatile and widely used austenitic stainless steel, 304L is the ultra low carbon variant of 304 stainless, while 304H is the high carbon version of the 304 stainless. Carbon content is the only chemical difference between these three grades, leading 304L to perform better in corrosive environments and be easier to weld.

Why Is 304L Easier To Weld Than 304?

Answer:

The lower carbon content in 304L helps to remove the chromium carbide precipitation that occurs during the welding, putting 304L at lower risk for intergranular corrosion even in highly corrosive environments.

What Is The Yield Strength Of This Grade Stainless Steel?

Answer:

The yield strength for 304 stainless is 205 MPa (30 ksi).

Related news

309S Stainless Steel Sheet & Coil Price List 2024/07/04

309S hot rolled stainless steel plate is engineered to provide outstanding resistance to oxidation and high-temperature environments. This grade is an austenitic chromium-nickel stainless steel, known for its ability to withstand temperatures up to 1900°F (1038°C).
More Details
904L

904L is a non-stabilised low carbon high alloy austenitic stainless steel, which designed for moderate to high corrosion resistance in a wide range of process environments. The addition of copper to this grade gives it greatly improved resistance to strong reducing acids, particularly sulphuric acid. The combination of high nickel and molybdenum content, assure good chloride stress corrosion cracking resistance, including pitting, crevice corrosion and stress corrosion cracking. Even down to cryogenic temperatures, the austenitic structure also gives 904L stainless steel excellent toughness, easily welded and processed by standard shop fabrication practices.
More Details
310MoLN

310MoLN is a high-alloy austenitic stainless steel with nitrogen, it helps to stabilize and strengthen the austenitic phase, and does not have intermetallic phases such as intergranular carbide precipitations. The material has excellent resistance to corrosion in ammonium carbamate and nitric acid, including intergranular corrosion, pitting and crevice corrosion. Also, 310MoLN stainless steel offers good weldability with a fairly high embodied energy and a fairly low ductility, widely used in applications that require excellent strength, oxidation resistance, and resistance to chloride-induced stress corrosion cracking.
More Details
316LVM Stainless Steel

The grade of 316LVM is a modified version of 316 with low carbon, high nickel and molybdenum. The purpose of the improvement of chemical composition is to maximize the corrosion resistance of the material by obtaining a ferrite free metallographic structure. In order to ensure purity and uniformity, the double vacuum smelting process (VIM+VAR) is generally adopted.
More Details
2507 Super Duplex Stainless Steel

2507 super duplex stainless steel contains 25% chromium, 4% molybdenum, and 7% nickel are designed for demanding applications which require exceptional strength and corrosion resistance, such as chemical process, petrochemical, and seawater equipment. The steel has excellent resistance to chloride stress corrosion cracking, high thermal conductivity, and a low coefficient of thermal expansion. The high chromium, molybdenum, and nickel levels provide excellent resistance to pitting, crevice, and general corrosion.
More Details
2205 Duplex Stainless Steel

2205 duplex stainless steel (2205 DSS) is a two-phase, ferritic-austenitic 22% chromium, 5 to 6% nickel, 3% molybdenum alloyed stainless steel. It contains about 40~50% ferrite in the annealed condition. 2205 has been a practical solution to chloride stress corrosion cracking problems experienced with 304/304L or 316/316L stainless. The high chromium, molybdenum and nitrogen contents provide corrosion resistance superior to 316/316L and 317L stainless in most environments. The design strength of 2205 is significantly higher than 316/316L, often permitting lighter wall construction.
More Details