Our products conform to GB, AISI, ASTM, DIN, EN, JIS standard for stainlesss steel coil, sheet and plate.
|
Product Name |
310/310S Stainless Steel Plate, 310/310S Stainless Steel Sheet |
|
Equivalent Grade |
310: AISI 310, UNS S31000, SAE 310, DIN 1.4841, SUS 310, X15CrNiSI25-21 |
|
310S: AISI 310S, UNS S31008, SAE 310S, DIN 1.4845, SUS 310S, X12CrNi25-21 |
|
|
Standard |
GB, AISI, ASTM, DIN, EN, JIS |
|
Process |
Hot Rolled, Cold Rolled, Forged |
|
Sizes |
Thickness: 0.3-200mm, Width: 10-4000mm |
|
Surface Treatment |
NO.1, 1D, 2D, 2B, NO.4, BA, HL, Mirror, Embossim, Sandblasted |
|
Fabricating |
Rolling, Bending, Sllitting, Decoiling, Cutting, Drilling, Punching, Beveling, Welding etc. |
|
Inspection |
SGS, TUV, BV, ABS, LR etc. |
|
Application |
Oil&Gas, Petroleum, Vessels, Ship Building, Water Treatment And Environmental Protection etc. |
310/310S stainless steel plate is a multi-purpose austenitic heat resistant stainless steel with high chromium and nicke. It is great ductility, oxidation resistance and good aqueous corrosion resistance, making it become the ideal choice for projects that require service at high temperature corrosion resistant applications.
| Single Sheet Of Rolling Specification | |||||||
| Thickness/Width | 1500 | 1800 | 2000 | 2200 | 2400 | 2500 | 3200 |
| 4-6mm | √ | √ | - | - | - | - | - |
| 6-10mm | √ | √ | √ | √ | √ | - | - |
| 11-12mm | √ | √ | √ | √ | √ | √ | √ |
| 13-14mm | √ | √ | √ | √ | √ | √ | √ |
| 17-25mm | √ | √ | √ | √ | √ | √ | √ |
| 26-70mm | √ | √ | √ | √ | √ | √ | √ |
| 71-120mm | special | special | special | special | special | special | special |
310/310S Stainless Steel Grade:
Heat uniformly at 1742 – 2192°F (950 – 1200°C). After hot forming a final anneal at 1832 – 2101°F (1000 – 1150°C) followed by rapid quenching is recommended.
310/310S Stainless Steel Grade:
Cold forming of pieces with long-term exposure to high temperatures is not recommended since the grade is subject to carbide precipitation.
310/310S Stainless Steel Grade:
It can be welded by most standard processes, including TIG, PLASMA, MIG, SMAW, SAW and FCAW.
|
|
C |
Mn |
P |
S |
Si |
Cr |
Ni |
Mo |
N |
Cu |
|
310 |
0.25 |
2.00 |
0.045 |
0.03 |
1.50 |
24.00-26.00 |
19.00-22.00 |
/ |
/ |
/ |
|
310S |
0.08 |
2.00 |
0.045 |
0.03 |
1.50 |
24.00-26.00 |
19.00-22.00 |
/ |
/ |
/ |
|
|
Tensile Strength (min) |
Yield Strength (min) |
Elongation |
Hardness, max |
|||
|
|
ksi |
Mpa |
ksi |
Mpa |
/ |
Brinell.HBW |
Rockwell |
|
310 |
75 |
515 |
30 |
205 |
40 |
217 |
95HRBW |
|
310S |
75 |
515 |
30 |
205 |
40 |
217 |
95HRBW |
What Is The Difference Between 310 And 310S?
Answer:
310S stainless steel has many of the same mechanical properties of 310 stainless steel, just contain lower levels of carbon. Lower carbon content is the only chemical difference between these two grades, leading 310S immune from sensitisation or grain boundary carbide precipitation, and easier to machine.
How Determine The Stainless Steel Grade For Your Needs?
Answer:
Magnetic Response — Some types of stainless steel grade are more magnetic than others. Adding chromium to a stainless steel tends to make it more magnetic, but adding nickel offsets or even eliminates the magnetism. Grade 310 are non-magnetic.
What Does It Mean To Be Austenitic?
Answer:
Austenitic stainless steels possess an austenitic microstructure. Their cells are in the shape of a cube with one atom at the corner of each cube and one in the middle. In crystallography, this is known as a face-centered crystal structure.Type 310/310S is a austenitic stainless steels, this grade has a high chromium and medium nickel content that makes it highly resistant to oxidation and corrosion. It is used for high temperature applications.