Our products conform to GB, AISI, ASTM, DIN, EN, JIS standard for stainlesss steel coil, sheet and plate.
Product Name |
410 Stainless Steel Coil, 410S Stainless Steel Coil |
Equivalent Grade |
410: AISI 410, UNS S41000, SAE 410, DIN 1.4006, SUS 410, X12Cr13 |
410S: AISI 410S, UNS S41008, SAE 410S, DIN 1.4024, SUS 410S, X6Cr13 |
|
Standard |
GB, AISI, ASTM, DIN, EN, JIS |
Process |
Hot Rolled, Cold Rolled |
Sizes |
Thickness: 0.1-16mm, Width: 600-2000mm |
Surface Treatment |
NO.1, 2B, NO.4, BA, HL, Mirror |
Inspection |
SGS, TUV, BV, ABS, LR etc. |
Packing |
Wooden Box, Wooden Pallet, Iron Frame |
Application |
Oil&Gas, Petroleum, Vessels, Ship Building, Water Treatment And Environmental Protection etc. |
410 stainless steel is a martensitic stainless steel known for its high strength, good corrosion resistance, and moderate impact toughness. 410s stainless steel is a low-carbon modification of 410 stainless steel, it offers improved weldability and formability while maintaining similar corrosion resistance and mechanical properties as 410 stainless steel. Both are widely used.
|
C |
Mn |
P |
S |
Si |
Cr |
Ni |
Mo |
N |
Cu |
410 |
0.15 |
1.00 |
0.04 |
0.03 |
1.00 |
11.50-13.50 |
0.60 |
/ |
/ |
/ |
410S |
0.08 |
1.00 |
0.04 |
0.03 |
1.00 |
11.50-13.50 |
0.60 |
/ |
/ |
/ |
|
Tensile Strength (min) |
Yield Strength (min) |
Elongation |
Hardness, max |
|||
|
ksi |
Mpa |
ksi |
Mpa |
/ |
Brinell.HBW |
Rockwell |
410 |
60 |
415 |
30 |
205 |
22 |
183 |
89HRBW |
410S |
60 |
415 |
30 |
205 |
22 |
183 |
89HRBW |
Hot rolling is a metalworking process. Such as steel ingots or billets are difficult to deform and process at room temperature, they are generally heated to 1100 to 1250° for rolling, this rolling process is called hot rolling. Most steel materials are rolled by hot rolling, the steel delivered in the hot-rolled state has a certain degree of corrosion resistance due to the high temperature, so it can bestored in the open air. In addition, hot rolling is that it can destroy the casting structure of the ingot, refine the grain of the steel, eliminate structural defects, make the steel structure dense, and improve the hardness of the hot rolled steel.
Cold rolling refers to a rolling process that uses the pressure of rolls to squeeze steel to change the shape of the steel at room temperature. The advantafe of cold rolling is fast forming speed, high output, the coating is not damaged, and it can be made into a variety of cross-sectional forms to meet the needs of the use conditions. In addition, cold rolling can cause large plastic deformation of the steel, thereby increasing the yield point of the steel. Which is Widely used in home appliances and other industries.
What Is The Difference Between 316 And 316L?
Answer:
316L stainless steel has many of the same mechanical properties of 316 stainless steel, just contain lower levels of carbon. Lower carbon content is the only chemical difference between these two grades, leading 316L immune from sensitisation or grain boundary carbide precipitation, and easier to machine.
What Are The Classes Of Stainless Steel?
Answer:
Classes of stainless steel are organized by their crystalline structure, mainly divided into martensitic, ferritic, austenitic, duplex, and precipitation-hardening. Austenitic is the most common, 321/321H is one of the austenitic stainless steel.
What Is Duplex Stainless Steel?
Answer:
Combining austenitic and ferritic stainless steels equally, duplex stainless steel contain chromium (21-27%), nickel (1.35-8% ), copper (0.05-3%), and molybdenum (0.05-5% ). The combination of elements makes duplex stainless steel stronger than either austenitic or ferritic steel by itself.