UNS N07080, Alloy 80A, W.Nr. 2.4631, Nimonic® 80A
Note that the designation “Nimonic®” is registered trademarks of Special Metals Corporation group of companies.
UNS N07080 is a wrought, age-hardenable nickel-chromium alloy, strengthened by additions of titanium, aluminum and carbon, developed for service at temperatures up to 815°C (1500°F). It is produced by high-frequency melting and casting in air for forms to be extruded.
Material |
Ni |
C |
Cr |
Si |
Cu |
Fe |
Mn |
Ti |
N07080 |
Balance |
0.10 max |
18.0-21.0 |
1.00 max |
0.20 max |
3.00 max |
1.00 max |
1.80-2.70 |
Material |
Tensile strength |
Yield strength 0,2 |
Elongation |
Hardness HB30 |
800-1000 N/mm² |
550-750 N/mm² |
30-40% |
200-250HB |
Aerospace Industry: Aircraft engine components, exhaust systems, and afterburner parts
Gas Turbines: Turbine blades, turbine discs, and combustor cans
Chemical Processing: Reactors, heat exchangers, and furnace components
Nuclear Industry: Reactor core components and fuel handling systems
Power Generation: Steam turbines and boiler components
Automotive Industry: Exhaust valves, turbocharger components, and piston rings
Nimonic 80A exhibits good corrosion resistance, particularly in high-temperature and corrosive environments. It demonstrates excellent oxidation resistance, making it suitable for high-temperature applications.Alloy 80A also withstands attack from acidic and alkaline environments, making it suitable for chemical processing. Additionally, it has resistance to stress corrosion cracking, making it suitable for applications under combined stress and corrosive conditions.
Nimonic 80A should be in the fully heat treated condition for all machining operations. The high material hardness in this condition requires the use of stringent machining techniques.
Nimonic 80A is readily joined by any of the resistance welding processes. For section thicknesses up to about 5 mm, fusion welding by conventional processes such as T.I.G. or M.I.G. is satisfactory. For section thicknesses greater than 5 mm, electron beam, friction, inertia and flash-butt welding have all been successfully used. The normal precautions for welding nickel alloys should be observed and welding should be carried out on solution treated material. Post-weld heat treatment is necessary to achieve optimum properties.
Ø Bar & Rod
Ø Plate & Sheet
Ø Coil & Strip
Ø Pipe & Tube
Ø Fitting: Flange, Tee, Elbow, Reducer etc.
Ø Forging: Ring, Shaft, Circle, Block etc.
Ronsco is a supplier with more than 27 years of experience in the stainless steel and nickel alloy field, we always adheres to the business phiosophy of "customer-centered", tries its best to meet the requirements of customers and pursues win-win cooperation with customers. Are you looking for metal products one-stop supplier! Contact Us Now! Email: service@ronsteel.com