Our products conform to GB, AISI, ASTM, DIN, EN, JIS standard for stainlesss steel coil, sheet and plate.
Product Name |
Stainless Steel Channel, Stainless Steel U Channel, Stainless Steel C Channel |
Standard |
GB, AISI, ASTM, DIN, EN, JIS |
Available Grades |
300 Series: 304, 304L, 304H, 309, 309S, 310, 310S, 316, 316L, 317, 317L, 321, 321H, 347, 347H |
400 Series: 409, 410S, 416, 420, 430, 439, 440, 444, 446 |
|
Duplex and Others: 2205, 2507, S31803, S32205, S32750, S32760, 253MA, 254SMO, 904L etc |
|
Process |
Hot Rolled, Cold Rolled |
Sizes |
Inquire For Sizes |
Surface Treatment |
NO.1, 2B, NO.4, BA, HL, Mirror |
Inspection |
SGS, TUV, BV, ABS, LR etc. |
Application |
Oil&Gas, Petroleum, Vessels, Ship Building, Water Treatment And Environmental Protection etc. |
C | Mn | P | S | Si | Cr | Ni | Mo | N | Cu | ||||||
304 | 0.07 | 2.00 | 0.045 | 0.03 | 0.75 | 17.50-19.50 | 8.00-10.5 | / | 0.10 | / | |||||
304L | 0.03 | 2.00 | 0.045 | 0.03 | 0.75 | 17.50-19.50 | 8.00-12.00 | / | 0.10 | / | |||||
304H | 0.10 | 2.00 | 0.045 | 0.03 | 0.75 | 17.50-19.50 | 8.00-10.5 | / | 0.10 | / | |||||
309 | 0.20 | 2.00 | 0.045 | 0.03 | 0.75 | 22.00-24.00 | 12.00-15.00 | / | / | / | |||||
309S | 0.08 | 2.00 | 0.045 | 0.03 | 0.75 | 22.00-24.00 | 12.00-15.00 | / | / | / | |||||
310 | 0.25 | 2.00 | 0.045 | 0.03 | 1.50 | 24.00-26.00 | 19.00-22.00 | / | / | / | |||||
310S | 0.08 | 2.00 | 0.045 | 0.03 | 1.50 | 24.00-26.00 | 19.00-22.00 | / | / | / | |||||
316 | 0.08 | 2.00 | 0.045 | 0.03 | 0.75 | 16.00-18.00 | 10.00-14.00 | 2.00-3.00 | 0.10 | / | |||||
316L | 0.03 | 2.00 | 0.045 | 0.03 | 0.75 | 16.00-18.00 | 10.00-14.00 | 2.00-3.00 | 0.10 | / | |||||
321 | 0.08 | 2.00 | 0.045 | 0.03 | 0.75 | 17.00-19.00 | 9.00-12.00 | / | 0.10 | / | |||||
321H | 0.10 | 2.00 | 0.045 | 0.03 | 0.75 | 17.00-19.00 | 9.00-12.00 | / | 0.10 | / | |||||
2205 | 0.03 | 2.00 | 0.03 | 0.02 | 1.00 | 22.00-23.00 | 4.50-6.50 | 3.00-5.00 | 0.14-0.20 | / | |||||
2507 | 0.03 | 1.20 | 0.035 | 0.02 | 0.80 | 24.00-26.00 | 6.00-8.00 | 3.00-5.00 | 0.24-0.32 | 0.50 | |||||
904L | 0.02 | 2.00 | 0.045 | 0.035 | 1.00 | 19.00-23.00 | 23.00-28.00 | 4.00-5.00 | 0.10 | 1.00-2.00 |
Tensile Strength (min) | Yield Strength (min) | Elongation | Hardness, max | ||||||||||||
ksi | Mpa | ksi | Mpa | / | Brinell.HBW | Rockwell | |||||||||
304 | 75 | 515 | 30 | 205 | 40 | 201 | 92HRBW | ||||||||
304L | 70 | 485 | 25 | 170 | 40 | 201 | 92HRBW | ||||||||
304H | 75 | 515 | 30 | 205 | 40 | 201 | 92HRBW | ||||||||
309 | 75 | 515 | 30 | 205 | 40 | 217 | 95HRBW | ||||||||
309S | 75 | 515 | 30 | 205 | 40 | 217 | 95HRBW | ||||||||
310 | 75 | 515 | 30 | 205 | 40 | 217 | 95HRBW | ||||||||
310S | 75 | 515 | 30 | 205 | 40 | 217 | 95HRBW | ||||||||
316 | 75 | 515 | 30 | 205 | 40 | 217 | 95HRBW | ||||||||
316L | 70 | 485 | 25 | 170 | 40 | 217 | 95HRBW | ||||||||
321 | 75 | 515 | 30 | 205 | 40 | 217 | 95HRBW | ||||||||
321H | 75 | 515 | 30 | 205 | 40 | 217 | 95HRBW | ||||||||
2205 | 95 | 655 | 65 | 450 | 25 | 293 | 31HRC | ||||||||
2507 | 116 | 795 | 80 | 550 | 15 | 310 | 32HRC | ||||||||
904L | 71 | 490 | 31 | 220 | 35 | / | 90HRBW |
Hot rolling is a metalworking process. Such as steel ingots or billets are difficult to deform and process at room temperature, they are generally heated to 1100 to 1250° for rolling, this rolling process is called hot rolling. Most steel materials are rolled by hot rolling, the steel delivered in the hot-rolled state has a certain degree of corrosion resistance due to the high temperature, so it can bestored in the open air. In addition, hot rolling is that it can destroy the casting structure of the ingot, refine the grain of the steel, eliminate structural defects, make the steel structure dense, and improve the hardness of the hot rolled steel.
Cold rolling refers to a rolling process that uses the pressure of rolls to squeeze steel to change the shape of the steel at room temperature. The advantafe of cold rolling is fast forming speed, high output, the coating is not damaged, and it can be made into a variety of cross-sectional forms to meet the needs of the use conditions. In addition, cold rolling can cause large plastic deformation of the steel, thereby increasing the yield point of the steel. Which is Widely used in home appliances and other industries.
What Is The Difference Between 304, 304L And 304H?
Answer:
304 is considered the most versatile and widely used austenitic stainless steel, 304L is the ultra low carbon variant of 304 stainless, while 304H is the high carbon version of the 304 stainless. Carbon content is the only chemical difference between these three grades, leading 304L to perform better in corrosive environments and be easier to weld.
Why Is 304L Easier To Weld Than 304?
Answer:
The lower carbon content in 304L helps to remove the chromium carbide precipitation that occurs during the welding, putting 304L at lower risk for intergranular corrosion even in highly corrosive environments.
What Is The Yield Strength Of This Grade Stainless Steel?
Answer:
The yield strength for 304 stainless is 205 MPa (30 ksi).